Magnesite brick

Product group
Refractory Bricks & Raw Materials
Origin
China

Zhengzhou Huachen Refractory Co., Ltd.

China
Zhengzhou Huachen Refractory Co., Ltd.

Supplier info

Business type
Manufacturer
Year established
2003
Location
China
Exports to
Worldwide

Magnesite brick, the content of magnesium oxide is more than 90%,periclaseas the main crystal phase of basical

refractory brick.

Magnesite with high temperature refractorness, high begining temperature of softing under loading,good alkali

resistance of slag.

According to differnence of the production technology and raw materials,it is names general magnesite brick

and fused magnesite brick.

Magnesite brick is mainly used for open hearth furnace,bottom and wall of the EAF,conventer, high temperature

tunnel kiln,cement kiln,lime kiln, glass furnace regenerator.

General Magnesite brick

Item MZ-91 MZ-92 MZ-93 MZ-94
Chemical composition % MgO ≥ 91 92 93 94.5
Chemical composition % SiO2 ≤ 4.0 3.5 2.5 2.0
Chemical composition % Fe2O3 ≤ 1.3 - - 1.2
Chemical composition % CaO ≤ 2.5 2.5 2.0 1.8
Apparent Porosity% ≤ 18 18 18 18
Bulk Density g/cm3 ≥ 2.86 2.90 2.95 2.92
Cold Crushing Strength Mpa ≥ 60 60 50 60
0.2Mpa Refractoriness Under Load T0.6 ℃ ≥1570 ≥1560 ≥1620 ≥1650
Permanent Linear Change On Reheating(%)1500℃X2h 0~+0.4 0~+0.4 0~+0.4 0~+0.4
Thermal Shock Resistances 100℃ water cycles ≥18 ≥18 ≥18 ≥18

Fused Magnesite brick

Item Behaviors
Item Fused Magnesia Brick
Item F MZ-95 F MZ-96 F MZ-97 F MZ-98
Chemical composition MgO % ≥9 4.5 ≥9 5.5 ≥9 6.5 ≥97.5
Chemical composition SiO2 % ≤1.5 ≤1.2 ≤1.0 ≤0.5
Chemical composition CaO % ≤1.5 ≤1.2 ≤1.2 ≤0.6
Apparent Porosity % ≤18 ≤18 ≤17 ≤15
Cold Crushing Strength Mpa ≥55 ≥60 ≥60 ≥60
0.2Mpa Refractoriness Under Load T0.6 ≥1650 ≥1680 ≥1700 ≥1700
Bulk Density g/cm3 ≥2.95 ≥3.0 ≥3.05 ≥3.05
Thermal Stability 950℃ Wind cycles ≥15 ≥20 ≥20 ≥20