YJS-525 rtv2 silicone rubber for concrete casting
- Product group
- Condensation Cure
Shenzhen YiJiaSan Silicone Co., Ltd.
YJS-525 is medium hardness silicone with hardness Shore A 25.It is widely used for resin, gypsum, concrete/cement and artificial stone molding.
YJS-525 is medium hardness silicone with hardness Shore A 25. It is a kind of two- component materials consisting of a flowable part A which when mixed with the curing agent or catalyst,cures at room temperature by a condensation recation. It is widely used for resin, gypsum, concrete/cement and artificial stone molding.
-Easy to demould
-Good resistance to tearing
-Good tear&tensile strength
-Dimensional stability in time ( deformation - shrinking only up to 0.3 % )
-Remarkable resistance to high temperatures (up to 200 - 220℃ )
-Final curing at room temperature
3. Technical datasheet
Typical general characteristics Inspection Method Value
Product data (Catalyzed A+B) Inspection Method YJS-525
Hardness Shore A 25±2
Mix Ratio A:B 100:2
Color / White
Pot life 25 ℃ (77F) 30-40mins
Curing time 25 ℃ (77F) 3-4 hours
Mixed viscosity mPa.s 25000±2000
Tear-strength kg/cm 25±2
Tensile-strength M.pa ≥3.8
Elongation % ≥460%
Shrinkage % ≤0.2%
Step 1: Prepare and clean the prototype.
You must make sure your original molds perfect. fix the original mold on a board , then using some assistant material(like cardpaper) to make a frame for to surround the prototype. The frame is no need ,if we make the mold by brushing way .
Step 2: Take the silicone and catalyst as the ratio 100:2 (silicone:catalyst=100:2) ,mix the silicone rubber and catalyst evenly.
*Notes: Molding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of flowing liquid and part B is the curing agent. Remember to mix part A and part B evenly, otherwise the silicon rubber will be partly solidified and this will bring troubles for your final operation. What’s more, the finished molds will have a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
After mixed the silicone evenly, it is better to release the bubble by Vacuum pumping.
Step 4: Pouring cast or brushing cast
After released the bubble, we can pour/brush the silicone rubber on the prototype
*Notes:Please finished all the steped within the operation time .If not it will cause cross linking reaction, and no more further steps will be available.So,we have to pay attention to the pot life and curing time.
Part A: Silicone rubber is a white liquid
Part B: Catalyst is a non-toxic and odorless liquid, white transparent color.
ATT: We can provide fast/medium/slow catalyst of for hot, warm or cold season.
When stored at or below 32°C (89.6°F) in the original unopened containers, YJS-5 series Silicone Base and its Curing Agents have a usable life of 10 months.
Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.
Curing Agent: 30g/bottle; 1kg/bottle
- Company name
- Shenzhen YiJiaSan Silicone Co., Ltd.
- Business type
- Year established
- Exports to
More from this supplier
brushable tin cure silicone rubber for mold making
YJS-520 easy demould rtv2 silicone rubber for tire mold
YJS-520 2 part liquid silicone rubber for soap&candle mold
YJS-515 RTV silicone mold making material for wax candle molds
YJS-510 Shore A 10 rtv2 silicone rubber for candle mold
YJS-505 soft liquid silicone rubber for soap mold making
YJS-520 shoe sole mold making liquid silicone rubber
YJS-525 rtv liquid molding silicone rubber for gypsum statue