YJS-535 high hardness rtv2 silikon for grc molding
- Product group
- Condensation Cure
Shenzhen YiJiaSan Silicone Co., Ltd.
YJS-535 is a type of hard silicone with hardness Shore A 35.It is widely used for making molds for artificial stone, gypsum casting, grc, grfc, cement/concrete decorative products and etc.
YJS-535 is a type of hard silicone with hardness Shore A 35. It is a kind of of two- component materials consisting of a flowable part A which when mixed with the curing agent or catalyst,cures at room temperature by a condensation reaction. It is widely used for making molds for artificial stone, gypsum casting, grc, grfc, cement/concrete decorative products and etc.
-Amazing fluidity and easy to operate
-Complex design available
-Stable quality, non-toxic and odorless catalyst provided
-Excellent tension and tear strength
-High performance in duplication
-Shrinkage is almost zero (below 0.2)
-Excellent resistance to weather, temperature, aging, acid and aging-proofing.
Typical general characteristics Inspection Method Value
Product data (Catalyzed A+B) Inspection Method YJS-535
Hardness Shore A 35±2
Mix Ratio A:B 100:2
Color / White
Pot life 25 ℃ (77F) 30-40mins
Curing time 25 ℃ (77F) 3-4 hours
Mixed viscosity mPa.s 25000±2000
Tear-strength kg/cm 25±2
Tensile-strength M.pa ≥4.1
Elongation % ≥420%
Shrinkage % ≤0.2%
4. Using instructions
Step 1: Prepare and clean the prototype.
You must make sure your original molds perfect. fix the original mold on a board , then using some assistant material(like cardpaper) to make a frame for to surround the prototype. The frame is no need ,if we make the mold by brushing way .
Step 2: Take the silicone and catalyst as the ratio 100:2 (silicone:catalyst=100:2) ,mix the silicone rubber and catalyst evenly.
*Notes: Molding silicon rubber is a kind of flowing liquid and it contains two parts. Part A is a kind of flowing liquid and part B is the curing agent. Remember to mix part A and part B evenly, otherwise the silicon rubber will be partly solidified and this will bring troubles for your final operation. What’s more, the finished molds will have a short life. All of these will cause a waste of silicon rubber.
Step 3: Vacuum pumping
After mixed the silicone evenly, it is better to release the bubble by Vacuum pumping.
Step 4: Pouring cast or brushing cast
After released the bubble, we can pour/brush the silicone rubber on the prototype
*Notes:Please finished all the steped within the operation time .If not it will cause cross linking reaction, and no more further steps will be available.So,we have to pay attention to the pot life and curing time.
Part A: Silicone rubber is a white liquid
Part B: Catalyst is a non-toxic and odorless liquid, white transparent color.
ATT: We can provide fast/medium/slow catalyst of for hot, warm or cold season.
When stored at or below 32°C (89.6°F) in the original unopened containers, YJS-5 series Silicone Base and its Curing Agents have a usable life of 12 months.
Silicone base:1kg/drum; 20kg/drum;25kg/drum;200kg/drum.
Curing Agent: 30g/bottle; 1kg/bottle
- Company name
- Shenzhen YiJiaSan Silicone Co., Ltd.
- Business type
- Year established
- Exports to
More from this supplier
brushable tin cure silicone rubber for mold making
YJS-520 easy demould rtv2 silicone rubber for tire mold
YJS-520 2 part liquid silicone rubber for soap&candle mold
YJS-515 RTV silicone mold making material for wax candle molds
YJS-510 Shore A 10 rtv2 silicone rubber for candle mold
YJS-505 soft liquid silicone rubber for soap mold making
YJS-520 shoe sole mold making liquid silicone rubber
YJS-525 rtv liquid molding silicone rubber for gypsum statue